ALUMINUM PLATES – ALLOY 5754 H111 & H22
Properties of Aluminum Alloy 5754
Aluminium plates – alloy 5754 H111 & H22 is an aluminum alloy with magnesium as the primary alloying element. It gives the alloy high ductility and elongation, also have very good corrosion resistance suitable for seawater and industrially polluted areas.
Applications of Aluminium plates – alloy 5754 H111 & H22
It is used for construction, marine and automotive applications. Suitable for anodizing. Application: Buildings: Roofing, Cladding, Signage, Road Signs, Furniture, Anodizing structure.
Table of commonly stocked sizes for Aluminum Alloy 5754
| Aluminum Plates 5754 Thickness (mm) | Size 1000mm x 2000mm | Size 1500mm x 3000mm |
| 1 | ✓ | ✓ |
| 1.5 | ✓ | ✓ |
| 2 | ✓ | ✓ |
| 3 | ✓ | ✓ |
| 4 | ✓ | ✓ |
| 5 | ✓ | ✓ |
| 8 | ✓ | ✓ |
| 10 | ✓ | ✓ |
| 12 | ✓ | ✓ |
| 15 | ✓ | ✓ |
Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.
Technical Datasheet of Aluminum Alloy 5754
Chemical Compositions of Aluminum Alloy 5754
| Element | Composition % |
| Manganese (Mn) | 0.0 – 0.50 |
| Ferrous (Fe) | 0.0 – 0.40 |
| Magnesium (Mg) | 2.60 – 3.60 |
| Silicone (Si) | 0.0 – 0.40 |
| Chromium (Cr) | 0.0 – 0.30 |
| Copper (Cu) | 0.0 – 0.10 |
| Manganese + Chromium (Mn+Cr)) | 0.10 – 0.60 |
| Other (Any) | 0.0 – 0.05 |
| Other (Total) | 0.0 – 0.15 |
| Titanium (Ti) | 0.0 – 0.15 |
| Zinc (Zn) | 0.0 – 0.20 |
| Aluminum (Al) | Balance |
Mechanical Properties of Aluminum Alloy 5754
| Properties | Value |
| Yield strength | 130 Min MPa |
| Ultimate tensile strength | 220-270 MPa |
| Elongation | 7 Min % |
| Brinell hardness | 63 HB |
Physical Properties of Aluminum Alloy 5754
| Properties | Value |
| Density | 2.66 g/cm3 |
| Melting point | 600°C |
| Thermal expansion | 24 ×10−6 /K |
| Modulus of elasticity | 68 GPa |
| Thermal conductivity | 147 W/m.K |
| Electrical resistance | 0.049 ×10−6Ω.m |
Aluminium Alloy 5754 Weldability
Good
Aluminium Alloy 5754 Fabrication/Machinability
Good