Aluminum Plates-Special Alloys

 Aluminium Plates – Alloy 5754 H111 & H22

Aluminium Alloy 5754  Aluminium Plate 5754

Properties of Aluminium Alloy 5754

5754 is an aluminum alloy with magnesium as the primary alloying element. It gives the alloy high ductility and elongation, also have very good corrosion resistance suitable for seawater and industrially polluted areas.

Applications of Aluminium Alloy 5754

It is used for construction, marine and automotive applications. Suitable for anodizing. Application: Buildings: Roofing, Cladding, Signage, Road Signs, Furniture, Anodizing structure.

Table of commonly stocked sizes for Aluminium Alloy 5754

Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.

Aluminium Plates 5754 Thickness (mm)

Size 1000mm x 2000mm

Size 1500mm x 3000mm

1.5

2

3

4

5

8

10

12

15

 

Technical Datasheet of Aluminium Alloy 5754

Chemical Compositions of Aluminium Alloy 5754

Element

Composition %

Manganese (Mn)

0.0 - 0.50

Iron (Fe)

0.0 - 0.40

Magnesium (Mg)

2.60 - 3.60

Silicon (Si)

0.0 - 0.40

Chromium (Cr)

0.0 - 0.30

Copper (Cu)

0.0 - 0.10

Manganese + Chromium (Mn+Cr)

0.10 - 0.60

Other (Each)

0.0 - 0.05

Others(Total)

0.0 - 0.15

Titanium (Ti)

0.0 - 0.15

Zinc (Zn)

0.0 - 0.20

Aluminium (Al)

Balance

Mechanical Properties of Aluminium Alloy 5754

Property

Value

Yield Strength

130 Min MPa

Tensile Strength

220-270 MPa

Elongation at brake

7 Min %

Hardness Brinell

63 HB

 

Physical Properties of Aluminium Alloy 5754

Property

Value

Density

2.66 g/cm3

Melting Point

600°C

Thermal Expansion

24 ×10−6 /K

Modulus of Elasticity

68 GPa

Thermal Conductivity

147 W/m.K

Electrical Resistivity

0.049 ×10−6Ω.m

 

Aluminium Alloy 5754 Weldability

Good

Aluminium Alloy 5754 Fabrication/Machinability

Good

</div

 Aluminium Plates- Alloy 2024 T3

Aluminium Plate 2024   Aluminium Plate 2024

Properties of Aluminium Alloy 2024

The 2024 alloy is often chosen for applications that require high strength. It is stronger than 6082 but less versatile. While 7075 is suited to applications that require high stress and strain resistance, 2024 has high cyclic fatigue resistance.

Applications of Aluminium Alloy 2024

The 2024 aluminum alloy is often used in aircraft structural applications due to its high strength and fatigue resistance. 2024 aluminum has excellent machinability, good workability, high strength, making it an optimal choice for aircraft and vehicle applications. 2024 aluminum is used throughout many industries.

Table of commonly stocked sizes for Aluminium Alloy 2024

Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.

Дебелина на Алуминиевите Листа

Размер 1000 мм х 2000 мм

Размер 1520 мм х 3020 мм

15

20

25

30

40

50

75

100

 

Technical Datasheet of Aluminium Alloy 2024

Chemical Compositions of Aluminium Alloy 2024

Element

Composition % 

Manganese (Mn)

1.20 - 1.80

Iron (Fe)

0.50 max

Copper (Cu)

3.80-4.90

Magnesium (Mg)

0.30 - 0.90

Silicon (Si)

0.50 max

Zinc (Zn)

0.25 max

Chromium (Cr)

0.10 max

Titanium (Ti)

0.15 max

Other  (Each)

0.0 - 0.05

Others (Total)

0.0 - 0.15

Aluminium (Al)

Balance

 

Mechanical Properties of Aluminium Alloy 2024

Property

Value

Yield Strength

345 Min MPa

Tensile Strength

483 MPa

Elongation at brake

20 Min %

Hardness Brinell

120 HB

 

Physical Properties of Aluminium Alloy 2024

Property

Value

Density

2.78 g/cm3

Melting Point

638°C

Thermal Expansion

23 ×10−6 /K

Modulus of Elasticity

73 GPa

Thermal Conductivity

121 W/m.K

Electrical Resistivity

0.058 ×10−6Ω.m

 

Aluminium Alloy 2024 Weldability

Poor

Aluminium Alloy 2024 Fabrication/Machinability

Good

 Aluminium Plates – Alloy 5083 H111 & H32

Aluminium Plate 5083   Aluminium Plate 5083

Properties of Aluminium Alloy 5083

Aluminium alloy 5083 is a high magnesium known for exceptional performance in extreme environments. In the tempered condition, it is strong, and retains good formability due to excellent ductility. 5083 is highly resistant to attack seawater and Industrial chemical environments. It also performs good strength after welding.

Applications of Aluminium Alloy 5083

Because of its strength and corrosion resistant properties of 5083 is widely used in the Ship Building industry. It is also preferably used in the following industries such as: Marine applications, Transportation, Pressure vessels, Cars.

Table of commonly stocked sizes for Aluminium Alloy 5083

Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.

Aluminium Sheet Thickness (mm) 

Size 1000mm x 2000mm

Size 1520mm x 3020mm 

15

20

25

30

40

50

75

100

 

Technical Datasheet of Aluminium Alloy 5083

Chemical Compositions of Aluminium Alloy 5083

Element

Composition % 

Manganese (Mn)

0.40 - 1.00

Iron (Fe)

0.40 max

Copper (Cu)

0.10 max

Magnesium (Mg)

4.00 - 4.90

Silicon (Si)

0.0 - 0.40

Zinc (Zn)

0.0 - 0.10

Chromium (Cr)

0.05 - 0.25

Titanium (Ti)

0.15 max

Other  (Each)

0.0 - 0.05

Others (Total)

0.0 - 0.15

Aluminium (Al)

Balance

 

Mechanical Properties of Aluminium Alloy 5083

Property

Value

Yield Strength

155 Min MPa

Tensile Strength

275-350 MPa

Elongation at brake

10 Min %

Hardness Brinell

75 HB

 

Physical Properties of Aluminium Alloy 5083

Property

Value

Density

2.65 g/cm3

Melting Point

570°C

Thermal Expansion

25 ×10−6 /K

Modulus of Elasticity

72 GPa

Thermal Conductivity

121 W/m.K

Electrical Resistivity

0.058 ×10−6Ω.m

 

Aluminium Alloy 5083 Weldability

Good

Aluminium Alloy 5083 Fabrication/Machinability

Good

 Aluminium Plates – Alloy 6082 T651

Aluminium Plate 6082   Aluminium Plate 6082   Aluminium Plate 6082

Properties of Aluminium Alloy 6082

Aluminium alloy 6082 is typically used in highly stressed applications. It is one of the more popular alloys in its series. Aluminium plates in 6082 are most commonly used for machining. As a relatively new alloy, the higher strength of 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy. It is excellent for anodizing, corrosion resistance and toughness.

Applications of Aluminium Alloy 6082

Due to its strength and corrosion resistance, alumiunium plates of alloy 6082 are typically used in construction, transport applications, bridges, cranes, hydraulic parts, marine and aircraft industry.

Table of common sizes for Aluminium Alloy 6082

Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.

Aluminium Sheet Thickness (mm) 

Size 1000mm x 2000mm

Size 1520mm x 3020mm 

15

20

25

30

40

50

75

100

 

Technical Datasheet of Aluminium Alloy 6082

Chemical Compositions of Aluminium Alloy 6082

Element

Composition % 

Manganese (Mn)

0.4 - 1.00

Iron (Fe)

0.0 - 0.50

Copper (Cu)

0.0 - 0.10

Magnesium (Mg)

0.60 - 1.20

Silicon (Si)

0.70 - 1.3

Zinc (Zn)

0.0 - 0.20

Chromium (Cr)

0.0 - 0.25

Titanium (Ti)

0.0 - 0.10

Other  (Each)

0.0 - 0.05

Others (Total)

0.0 - 0.15

Aluminium (Al)

Balance

 

Mechanical Properties of Aluminium Alloy 6082

Property

Value

Yield Strength

255 Min MPa

Tensile Strength

300 Min MPa

Elongation at brake

9 Min %

Hardness Brinell

91 HB

 

Physical Properties of Aluminium Alloy 6082

Property

Value

Density

2.70 g/cm3

Melting Point

555°C

Thermal Expansion

24×10−6 /K

Modulus of Elasticity

70 GPa

Thermal Conductivity

180 W/m.K

Electrical Resistivity

0.038 ×10−6Ω.m

 

Aluminium Alloy 6082 Weldability

Good

Aluminium Alloy 6082 Fabrication/Machinability

Good

 Aluminium Plates – Alloy 7075 T651

Aluminium Plate 7075   Aluminium Plate 7075

Properties of Aluminium Alloy 7075

Aluminium alloy 7075 is one of the strongest aluminum alloys available, it can match the strength of many steels while giving a considerable weight saving advantage. 7075 is produced from mixing Aluminium with Zinc, Magnesium and Copper, this alloy is tough workable and light. It also has excellent properties at low temperatures.

Applications of Aluminium Alloy 7075

Due to its strength this alloy is often used in molds for tools, bike frames and other sports equipment. Alloy 7075 is also commonly used in the automotive, aerospace and defense applications and high-risk applications (military, skyscrapers). The fatigue strength of the alloy is also important for repetitive loadings, such as in aviation or motor vehicles.

Table of common sizes for Aluminium Alloy 7075

Apart from these sizes, other nonstandard sizes are available on request. Please get in touch with us with your demand.

Aluminium Sheet Thickness (mm) 

Size 1000mm x 2000mm

Size 1520mm x 3020mm 

15

20

25

30

40

50

75

100

150

 

Technical Datasheet of Aluminium Alloy 7075

 

Chemical Compositions of Aluminium Alloy 7075

Element

Composition % 

Manganese (Mn)

0.05 - 0.30

Iron (Fe)

0.10 - 0.50

Copper (Cu)

1.2 - 2.0

Magnesium (Mg)

2.10 - 2.90

Silicon (Si)

0.10 - 0.40

Zinc (Zn)

5.10 - 6.10

Chromium (Cr)

0.15 - 0.28

Titanium (Ti)

0.01 - 0.20

Gallium (Ga)

0.01 - 0.05

Vanadium (V)

0.01 - 0.06

Aluminium (Al)

Balance

 

Mechanical Properties of Aluminium Alloy 7075

Свойства

Стойност

Yield Strength

500 Min MPa

Tensile Strength

572 Min MPa

Elongation at brake

3-9 Min %

Hardness Brinell

155 HB

 

Physical Properties of Aluminium Alloy 7075

Property

Value

Density

2.81 g/cm3

Melting Point

635°C

Thermal Expansion

23.6×10−6 /K

Modulus of Elasticity

72 GPa

Thermal Conductivity

130 W/m.K

Electrical Resistivity

0.0515 ×10−6Ω.m

 

Aluminium Alloy 7075 Weldability

Good

Aluminium Alloy 7075 Fabrication/Machinability

Good